Influence of Operational Strategies for the Recovery of Magnesium Hydroxide from Brines at a Pilot Scale
2022
The continuous depletion of minerals caused by land mining and the increase in their demand have pushed the development of novel sustainable technological processes for mineral recovery from unconventional sources. In this context, magnesium (Mg) has gained considerable attention for its peculiar properties and high relevance of its compounds, such as magnesium hydroxide, Mg(OH)2. In the present work, the influence of several operating conditions on the Mg(OH)2 precipitation process was thoroughly investigated by adopting a novel multiple feed-plug flow reactor. The influence of (i) initial Mg2+ concentrations in the feed stream; (ii) brine and alkaline flow rates; and (iii) the product rec…
Antifouling Mortars for Underwater Restoration
2022
This research has focused on the assessment of the compositional features and mechanical and antifouling performances of two different mortars formulated for an underwater setting, and which contain Mg(OH)2 as an antifouling agent. Regarding the mechanical characterization, the uniaxial compressive strength and flexural strength were measured. The composition of the materials was explored by differential thermal/thermogravimetric analysis (DTA-TG), X-ray diffraction analysis (XRPD), and scanning electronic microscopy (SEM) coupled with EDS microanalysis. The assessment of the biological colonization was evaluated with colorimetric analysis and image analysis. The results suggest that both m…
Development of a pilot plant for the recovery of magnesium hydroxide from waste brines
Waste brines from various industrial processes, mainly from saltworks, are an important source of minerals, such as magnesium, table salt and potable water.
Initial Surface Film on Magnesium Metal. A Characterization by X-ray Photoelectron Spectroscopy (XPS) and Photocurrent Spectroscopy (PCS)
2007
Abstract A detailed investigation of the initial film grown on mechanically polished Mg electrodes has been carried out by ex situ X-ray Photoelectron Spectroscopy (XPS) and in situ Photocurrent Spectroscopy (PCS), allowing to reach a detailed picture of the passive layer structure. The XPS data show that the films formed soon after mechanical treatment and immersion in aqueous electrolyte have a bilayer structure, consisting of an ultra-thin MgO inner layer (∼2.5 nm) and a Mg(OH) 2 external layer. The thickness of the Mg(OH) 2 layer is a function of immersion time and solution temperature. After mechanical treatment and immersion in aqueous solution at room temperature, the MgO/Mg(OH) 2 la…